Low Alloyed Tool Steel Plate, DIN 142W13
Delivery term:The date of payment from buyers deliver within days-
Price:
Negotiable
- minimum:
- Total supply:
-
Delivery term:
The date of payment from buyers deliver within days
-
seat:
Beijing
-
Validity to:
Long-term effective
-
Last update:
2017-07-21 16:45
-
Browse the number:
72
+
Shanghai Bozhong Metal Group Co. Ltd
- Contactaixin:
Contactaixin:
bozhong(Ms.)
- telephone:
-
Area:
Beijing
Address:BUILDING 32#, NO. 518, XINZHUAN ROAD, SONGJIANG, Shanghai, Shanghai, China (201612)
- Website:
+
Model Number: ZXL105
Brand Name: Baosteel, TISCO
Key Specifications/Special Features:
DescriptionLow alloyed W cold working tool steelApplicationsCutting tools, stamping, woodworking, drawing, deep drawing and pressing tools, cold working rolls, measuring toolsPhysical properties (average values) at ambient temperatureModulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 8.0
Chemical composition ( in weight%)
C: 1.43
Si: 0.23
Mn: 0.30
Cr: 0.35
V: 0.25
W: 3.05
Soft annealing
Heat to 720 to 750°C, cool slowly in furnace, this will produce a maximum Brinell hardness of 270
Stress relieving
Stress relieving to remove machining stresses should be carried out by heating to approx 650°C, holding for 1-2 hours at heat, followed by air cooling
This operation is performed to reduce distortion during heat treatment
Hardening
Harden from temperature of 800 to 830°C followed by water quenching, hardness after quenching is 66 HRC
Tempering
Tempering temperature: 100 to 250°C
Forging
Hot forming temperature: 1050 to 850°C
Specifications:
Grades: DIN 142W13
Standards: DIN, GB
Length: 1500-6000mm
Width: 100-1250mm
Thickness: 0.3-200mm
Certification: ISO
Technical treatment: cold-rolled and hot-rolled
Packing and delivery
Packing: standard export seaworthy package or as customer’s requirements
Delivery: 7-20 days after received deposit of T/T
Density [g/cm3]: 8.0
Chemical composition ( in weight%)
C: 1.43
Si: 0.23
Mn: 0.30
Cr: 0.35
V: 0.25
W: 3.05
Soft annealing
Heat to 720 to 750°C, cool slowly in furnace, this will produce a maximum Brinell hardness of 270
Stress relieving
Stress relieving to remove machining stresses should be carried out by heating to approx 650°C, holding for 1-2 hours at heat, followed by air cooling
This operation is performed to reduce distortion during heat treatment
Hardening
Harden from temperature of 800 to 830°C followed by water quenching, hardness after quenching is 66 HRC
Tempering
Tempering temperature: 100 to 250°C
Forging
Hot forming temperature: 1050 to 850°C
Specifications:
Grades: DIN 142W13
Standards: DIN, GB
Length: 1500-6000mm
Width: 100-1250mm
Thickness: 0.3-200mm
Certification: ISO
Technical treatment: cold-rolled and hot-rolled
Packing and delivery
Packing: standard export seaworthy package or as customer’s requirements
Delivery: 7-20 days after received deposit of T/T
Shipping Information:
- FOB Port: Shanghai
- Lead Time: 7 - 15 days
- Dimensions per Unit: 6 × 2 × 0.2 Meters
- Weight per Unit: 20 Kilograms
- Units per Export Carton: 5
- Export Carton Dimensions L/W/H: 6 × 2 × 0.2 Meters
- Export Carton Weight: 5 Tons (US)
Main Export Markets:
- Asia
- Australasia
- Central/South America
- Eastern Europe
- Mid East/Africa
- North America
- Western Europe